Self-aligned LDD thin-film transistor and method of fabricating the same

ABSTRACT

A self-aligned LDD TFT and a fabrication method thereof. A substrate is provided, on which a semiconductor layer is formed. A first masking layer is provided over a first region of the portion of the semiconductor layer. The first masking layer comprises a material that provides a permeable barrier to a dopant. The semiconductor layer including the first region covered by the first masking layer is exposed to the dopant, wherein the first region covered by the first masking layer is lightly doped with the dopant in comparison to a second region not covered by the first masking region.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The invention relates to a TFT, and more particularly to a TFT with a self-aligned LDD and a method for fabricating the same.

[0003] 2. Description of the Related Art

[0004] Thin-film transistors (TFTs) are widely used in active matrix liquid crystal display (AMLCD). A leakage current occurs, however, when the TFT is turned off, and the charges in the active matrix liquid crystal display are thereby lost. A lightly doped drain (LDD) structure has been used to reduce the electric field of the surface of the drain, such that the leakage current can be reduced.

[0005] In FIGS. 1A to 1B are cross-sections of the conventional method for fabricating a TFT with a self-aligned LDD.

[0006] In FIG. 1A, a transparent insulating substrate 101 is provided, a semiconductor layer 102 and a gate insulating layer 104 formed on the substrate 101, and the semiconductor layer 102 is covered by the gate insulating layer 104.

[0007] A patterned photoresist layer 106 is formed on the gate insulating layer 104. Heavy doping is performed on the semiconductor layer 102 to form a heavily doped region 108 as a source/drain (S/D) region except in the region covered by the photoresist layer 106.

[0008] In FIG. 1B, the photoresist layer 106 is removed. A gate layer 120 (e.g., a conductive layer) is formed on the gate insulating layer 104, and the gate layer 120 covers a portion of the undoped region of the semiconductor layer 102. Light doping is performed on the undoped region of the semiconductor layer 102 to form a LDD region using the gate layer 120 as a mask. The region of the semiconductor layer 102 a that is covered by the gate layer 120 is a channel.

[0009] The pattern in the photoresist layer 106 defined by an additional mask in the conventional method results in a process that requires a separate masking step and doping procedure for forming the LDD region, which region is easily shifted by misalignment of the mask such that the electrical properties of TFT are affected.

SUMMARY OF THE INVENTION

[0010] The present invention provides a process of forming a semiconductor device, which comprises heavily doped and lightly doped regions in a semiconductor layer formed in a single doping operation. This is accomplished by providing a masking layer having a relatively thicker section that corresponds to a region to be lightly doped, in comparison to a region that is heavily doped.

[0011] In one embodiment of the present invention, a masking layer covers the region of the semiconductor layer to be lightly doped and exposes the region of the semiconductor layer to be heavily doped during the doping process. The masking layer is permeable to dopant, but provides a barrier to the dopant such that the covered region is lightly doped compared to the heavily doped region. The thickness of the mask is chosen in relation to the doping parameters (e.g., time, dopant, concentration, etc.) to result in the desired doping levels in the lightly doped region and the heavily doped region in a single doping operation.

[0012] In another aspect of the present invention, it is directed to a self-aligned LDD TFT and a method for fabricating the same. LDD region of the present invention is formed by controlling the width and/or width of the gate insulating layer using only one mask.

[0013] In another aspect, the present invention provides a LDD TFT having a multi-gate structure, in which LDD regions are formed laterally adjacent to two sidewalls of each gate layer in the multi-gate structure. Each gate structure is formed with LDD and highly doped regions in accordance with the present invention, and two adjacent gate structures are interconnected by a common doped region having a different dopant concentration as the LDD region. In one embodiment, the common doped region is higher dope concentration than the LDD region, but lower dope concentration as the highly doped region. The common doped region may be formed by applying a shielding mask during an intermediate doping step between formation of LDD and highly doped regions.

[0014] Accordingly, the present invention provides a self-aligned LDD TFT. The TFT comprises a substrate, a semiconductor layer, a gate insulating layer, and a gate. The semiconductor layer having a channel is formed on the substrate, a first doping region is formed on both sides of the channel region, and a second doping region is formed on both sides of the first doping region. The gate insulating layer is formed, covering the semiconductor layer, and the gate insulating layer covers the channel region and the first doping region. The gate is formed on the gate insulating layer corresponding to the channel region.

[0015] Accordingly, the present invention also provides a LDD TFT having a multi-gate structure. An active layer is formed on a substrate and comprises a first lightly doped region, a second lightly doped region, and a third lightly doped region formed laterally adjacent to the first lightly doped region respectively, a first channel region and a second channel region extending laterally away from the second lightly doped region and the third lightly doped region respectively, a fourth lightly doped region and a fifth lightly doped region extending laterally away from the first channel region and the second channel region respectively, and a first heavily doped region and a second heavily doped region extending laterally away from the fourth lightly doped region and the fifth lightly doped region, respectively. A first gate insulating layer is formed on the active layer and comprises a central region covering the first channel region of the active layer, a first shielding region covering the fourth lightly doped region of the active layer, and a second shielding region covering the second lightly doped region of the active layer. A second gate insulating layer is formed on the active layer and comprises a central region covering the second channel region of the active layer, a first shielding region covering the third lightly doped region of the active layer, and a second shielding region covering the fifth lightly doped region of the active layer. A first gate layer covers the central region of the first gate insulating layer, and a second gate layer covers the central region of the second gate insulating layer.

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] For a better understanding of the present invention, reference is made to a detailed description to be read in conjunction with the accompanying drawings, in which:

[0017]FIGS. 1A to 1B are cross-sections illustrating the steps of the conventional method for fabricating a self-aligned LDD TFT;

[0018]FIGS. 2A to 2F are cross-sections illustrating the steps of the method for fabricating a self-aligned LDD TFT in accordance with the first embodiment of the present invention;

[0019]FIGS. 3A to 3E are cross-sections of a fabrication method for a LDD TFT having a dual-gate structure according to the second embodiment of the present invention;

[0020]FIG. 4 is a schematic diagram of a display device comprising the LDD TFT in accordance with one embodiment of the present invention; and

[0021]FIG. 5 is a schematic diagram of an electronic device comprising the display device in accordance with the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0022] The present invention provides a process for forming a semiconductor device, in which heavily doped and lightly doped regions are simultaneously formed in a semiconductor layer during doping operation. This is accomplished by providing a masking layer having a relatively thicker section that correspond to a region to be lightly doped, in comparison to a region that is heavily doped. By way of example and not limitations, the present invention is described below in connection with the formation of an LDD TFT.

[0023] In one embodiment of the present invention, a masking layer covers the region of the semiconductor layer to be lightly doped and exposes the region of the semiconductor layer to be heavily doped during the doping process. The masking layer is permeable to dopant, but provides a barrier to the dopant such that the covered region is lightly doped compared to the heavily doped region. The thickness of the masking layer is chosen in relation to the doping parameters (e.g., doping time, concentration, dopant, etc.) to result in the desired doping levels in the lightly doped region and the heavily doped region. This embodiment is illustrated in reference to FIGS. 2A to 2F below. It is noted that intermediate and/or additional steps and structures maybe included without departing from the scope and spirit of the present invention, but they are omitted from the drawings to avoid obscuring the disclosure of the present invention.

FIRST EMBODIMENT

[0024]FIGS. 2A to 2F are cross-sections illustrating the steps of the method for fabricating a self-aligned LDD TFT in accordance with the first embodiment of the present invention.

[0025] In FIG. 2A, a substrate 201, such as a transparent insulating substrate or glass substrate, is provided. A buffer layer 202, such as a silicon oxide layer, and a semiconductor layer 203, such as a polysilicon layer, are sequentially formed on the substrate 201. The buffer layer 202 helps the formation of the semiconductor layer 203 on the substrate 201.

[0026] In FIG. 2B, a gate insulating layer 204, such as an oxide layer or a nitride layer, a conductive layer 205, such as a metal layer, and a patterned photoresist layer 206 for forming a gate, are sequentially formed on the semiconductor layer 203. The thickness of the gate insulating layer 204 is about 200 to 10000 Å.

[0027] In FIG. 2C, the conductive layer 205 and the gate insulating layer 204 are sequentially etched until the semiconductor layer 203 is exposed to form a conducting layer 205 a and a gate insulating layer 204 a. The etching can be plasma etching.

[0028] In FIG. 2D, the conductive layer 205 a is etched by a gas mixture of oxygen-containing gas and other gas, such as chlorine-containing gas, to form a conductive layer 205 b as a gate so as to expose a portion of the gate insulating layer 204 a synchronously.

[0029] The flow rate of the oxygen in the gas mixture can be adjusted, and the etching step shown in FIG. 2C can be omitted or combined with the etching step shown in FIG. 2D to reduce processing time. In this case, the conductive layer 205 a and the gate insulating layer 204 a are etched by a minimum flow of oxygen, and the conductive layer 205 a is etched to form a trapezoid gate, by increasing the flow rate of oxygen, even a maximum oxygen flow.

[0030] In FIG. 2E, the patterned photoresist layer 206 b is removed. The semiconductor layer 203 is ion implanted with about 30 to 100 kev energy using the conducting layer 205 b and the gate insulating layer 204 a as masks to form a first doped region 203 b as lightly doped drain (LDD) and a second doped region 203 c as source/drain (S/D).

[0031] In FIG. 2F, the first doped region 203 b is formed in the semiconductor layer 203, covered by the gate insulating layer 204 a but not the conductive layer 205 b. The second doped region 203 c is formed in the semiconductor layer 203 covered by the gate insulating layer 204 a and the conductive layer 205 b.

[0032] The concentration of the first doped region 203 b is lower than in the second doped region 203 c because the first doped region 203 b is covered by the gate insulating layer 204 a and the second doped region 203 c is not covered by the gate insulating layer 204 a. By appropriately defining the thickness of the gate insulating layer 204 a in relation to the doping process parameters (e.g., dopant, doping time, concentration, etc.), the desired doping concentrations in the first and second doped regions 203 b and 203 c may be achieved when they are exposed to the same doping operation, e.g., using the same doping process parameters.

[0033] For certain applications, it may be desired to alter the doping process parameters and/or using a different or additional mask during the doping process. For example, after initial doping to form the lightly and heavily doped regions using a particular dopant concentration, a mask may be applied to cover the lightly doped region. Such variation is well within the scope and spirit of the present invention.

[0034]FIG. 2F is a simplified basic LDD TFT configuration, including a drain, source and a channel. Further steps to complete the may include steps to form, for example, electrodes, metalization, interconnect structures, passivation layers, etc. known in the art.

[0035] In a case of a TFT with CMOS, the semiconductor layer 203 is heavily implanted with P or As ions to form S/D, a second doped area 203 c, and a first doped region 203 b. The concentration of S/D and the second doped region 203 c are about 1×10¹⁴˜1×10¹⁶ atom/cm², and the concentration of the first doped region 203 b is about 1×10¹²˜1×10¹⁴ atom/cm².

[0036] The present invention also provides a LDD TFT having a multi-gate structure and a fabrication method thereof. A gate insulating layer comprises two shielding regions laterally exposed to a gate layer and used as a mask, such that LDD regions and source/drain regions can be completed in an ion implantation process simultaneously. Also, the LDD regions are formed laterally adjacent to two sidewalls of each gate layer in the multi-gate structure, thus effectively restraining leakage current and eliminating placement shifting and length-asymmetry problems caused by the photo misalignment. A LDD TFT having a dual-gate structure is described below for example.

SECOND EMBODIMENT

[0037]FIGS. 3A to 3E are cross-sections of a fabrication method for a LDD TFT having a dual-gate structure according to this embodiment.

[0038] In FIG. 3A, a substrate 30 is provided with a buffer layer 32 and a semiconductor layer 34 successively formed thereon. The substrate 30 is a transparent insulating substrate, such as a glass substrate. The buffer layer 32 is a dielectric layer, such as a silicon oxide layer, for improving the formation of the semiconductor layer 34 on the substrate 30. The semiconductor layer 34 is a polysilicon layer. In order to adjust threshold voltage of transistor, B⁺ or P⁺ ion implantation process may be performed thereon.

[0039] In FIG. 3B, an insulating layer 36 and a conductive layer 38 are successively deposited on the semiconductor layer 34. The insulating layer 36 may be made of silicon oxide, silicon nitride, silicon-oxide-nitride or a combination thereof. The conductive layer 38 (not shown) may be a metal layer or a polysilicon layer. Dry etching with a patterned photoresist mask then forms the conductive layer 38 as a first gate layer 38I and a second gate layer 38II. In FIG. 3C, plasma etching or reactive ion etching is employed with a reactive gas mixture of an oxygen-containing gas and a chlorine-containing gas, whereby the gate layers 38I and 38II of a trapezoid profile and two isolated gate insulating layers 40 and 42 are completed by adjusting the individual flow of the oxygen-containing gas or the chlorine-containing gas in a timely manner. For example, during the etching process for the gate layers 38I and 38II, the flow of the chlorine-containing gas is gradually tuned to a maximum, even if chlorine-containing gas is the only gas used. During the etching process for the insulating layer 36, the flow of the oxygen-containing gas is gradually increased to a maximum, such that a part of the patterned photoresist mask is removed and the gate layers 38I and 38II exposed again by the patterned photoresist mask is etched simultaneously. The photoresist mask is then removed.

[0040] The first gate insulating layer 40 comprises a central region 40 a and two shielding regions 40 b ₁ and 40 b ₂. The central region 40 a is covered by the bottom of the first gate layer 38I. The two shielding regions 40 b ₁ and 40 b ₂ extend laterally away from the central region 40 a, respectively, without being covered by the first gate layer 38I. The first gate insulating layer 40 exposes a predetermined source/drain region. The first shielding region 40 b ₁ has a lateral length W₁ of 0.1 μm˜2.0 μm, and the second shielding region 40 b ₂ a lateral length W₂ of 0.1 μm˜2.0 μm. Depending on requirements for circuit designs, the size and symmetry of the lateral lengths W₁ and W₂ may be adequately modified.

[0041] The second gate insulating layer 42 comprises a central region 42 a and two shielding regions 42 b ₁ and 42 b ₂. The central region 42 a is covered by the bottom of the second gate layer 38II. The two shielding regions 42 b ₁ and 42 b ₂ extend laterally away from the central region 42 a, respectively, without being covered by the second gate layer 38II. The second gate insulating layer 42 exposes a predetermined source/drain region. The first shielding region 42 b ₁ has a lateral length D₁ of 0.1 μm˜2.0 μm, and the second shielding region 42 b ₂ has a lateral length D₂ of 0.1 μm˜2.0 μm. Depending on requirements for circuit designs, the size and symmetry of the lateral lengths W₁, W₂, D₁ and D₂ may be adequately modified. For example, W₁=W₂ and D₁=D₂.

[0042] The second shielding region 40 b ₂ of the first gate insulating layer 40 is located adjacent to the first shielding region 42 b ₁ of the second gate insulating layer 42, and a space between the second shielding region 40 b ₂ and the first shielding region 42 b ₁ exposes the active layer 34. Also, the active layer 34 outside the first shielding region 40 b ₁ of the first gate insulating layer 40 and the second shielding region 42 b ₂ of the second gate insulating layer 42 is exposed.

[0043] In FIG. 3D, a lightly doped ion implantation process 44 is employed, and the gate layers 38I and 38II and the shielding regions 40 b ₁, 40 b ₂, 42 b ₁ and 42 b ₂ are used as masks, such that a plurality of regions 341˜349 with various doping concentrations is formed in the active layer 34. The first region 341 and the second region 342 are undoped, correspondingly located underlying the central regions 40 a and 42 a, respectively. The third region 343 and the fourth region 344 are N⁻⁻ regions, correspondingly located underlying the shielding regions 40 b ₁ and 40 b ₂, respectively. The fifth region 345 and the sixth region 346 are N⁻⁻ regions, correspondingly located underlying the shielding regions 42 b ₁ and 42 b ₂, respectively. The seventh region 347 is an N⁻ region exposed laterally adjacent to the first shielding region 40 b ₁ of the first gate insulating layer 40. The eighth region 348 is an N⁻ region exposed laterally adjacent to the second shielding region 42 b ₂ of the second gate insulating layer 42. The ninth region 349 is an N⁻ region exposed in the space between the shielding regions 40 b ₂ and 42 b ₁. Since the shielding regions 40 b ₁ and 40 b ₂ are used as masks, the margins of the regions 343 and 344 are substantially aligned to the edges of the shielding regions 40 b ₁ and 40 b ₂, respectively. Since the shielding regions 42 b ₁ and 42 b ₂ are used as masks, the margins of the regions 345 and 346 are substantially aligned to the edges of the shielding regions 42 b ₁ and 42 b ₂ respectively. In addition, by adjusting accelerated voltage and dosage of the lightly doped ion implantation process 44, the doping concentrations of the regions 343, 344, 345 and 346 can be modified to become N⁻⁻ regions or intrinsic regions (offset regions).

[0044] In FIG. 3E, a photoresist layer 46 is formed to cover the second shielding region 40 b ₂ of the first gate insulating layer 40, the first shielding region 42 b ₁ of the second gate insulating layer 42, and the ninth region 349 exposed in the space between the shielding regions 40 b ₂ and 42 b ₁. Finally, a heavily-doped ion implantation process 48 is performed, and the photoresist layer 46, the gate layers 38I and 38II, and the shielding regions 40 b ₁ and 42 b ₂ are used as masks, such that the doping concentrations of the regions 343 and 346 are increased to become N⁻ regions and the doping concentrations of the regions 347 and 348 are increased to become N⁺ regions.

[0045] Accordingly, the seventh region 347 and the eighth region 348 are N⁺ regions, serving as a source region and a drain region respectively. The third region 343 and the sixth region 346 are N⁻ regions, serving as two LDD regions. The fourth region 344 and the fifth region 345 are N⁻⁻ regions, serving as another two LDD regions, located between the two gate layers 38I and 38II. The ninth region 349 is an N⁻ region, serving as common source/drain region. The first region 341 and the second region 342 are undoped, serving as two channel regions of the dual-gate structure. Preferably, the doping concentration for regions 347 and 348 is 1×10¹⁴˜1×10¹⁶ atom/cm², for regions 343, 346 and 349, 1×10¹²˜1×10¹⁴ atom/cm², and for regions 344 and 345, less than 1×10¹³ atom/cm².

[0046] The LDD TFT may be used in a N-MOS TFT, such that the lightly doped regions are N⁻ regions, and heavily doped regions are N⁺ regions. Alternatively, the LDD TFT is used in a P-MOS TFT, such that the lightly doped regions are P⁻ regions, and heavily doped regions are P⁺ regions. Subsequent interconnect process including formation of inter-dielectric layers, contact holes and interconnects on the thin film transistor is omitted herein.

[0047] The LDD TFT and the fabrication method thereof have the following advantages.

[0048] First, two symmetrical LDD regions outside the two gate layers 38I and 38II and two symmetrical LDD regions between the two gate layers 38I and 38II are formed simultaneously, thus effectively reducing current leakage.

[0049] Second, the ion implantation process uses the shielding regions 40 b ₁, 40 b ₂, 42 b ₁ and 42 b ₂ as masks, thus completing self-aligned LDD regions and source/drain regions simultaneously.

[0050] Third, by adjusting parameters of the etching process, the lateral lengths W₁, W₂, D₁ and D₂ of the shielding regions 40 b ₁, 40 b ₂, 42 b ₁ and 42 b ₂ can be accurately controlled, thus ensuring proper positioning of the LDD structure and electric performance of the LDD TFT.

[0051] Fourth, since an extra photomask or a spacer structure for defining the LDD regions are not used, shifting of the LDD regions due to photo misalignment in exposure is prevented, further improving accuracy in positioning the LDD regions.

[0052] Fifth, the heavily doped ion implantation process 48 uses the photoresist layer 46 as a mask without a high-accuracy pattern, thus simplifying a photolithography process for the photoresist layer 46.

[0053]FIG. 3E is a simplified basic LDD TFT having a multi-gate structure configuration. Further steps to complete the LDD TFT may include steps to form, for example, electrodes, metalization, interconnect structures, passivation layers, etc. known in the art.

[0054]FIG. 4 is a schematic diagram of a display device 3 comprising the LDD TFT in accordance with one embodiment of the present invention. The display panel 1 can be couple to a controller 2, forming a display device 3 as shown in FIG. 4. The controller 3 can comprise a source and a gate driving circuits (not shown) to control the display panel 1 to render image in accordance with an input.

[0055]FIG. 5 is a schematic diagram of an electronic device 5, incorporating a display comprising the LDD TFT in accordance with one embodiment of the present invention. An input device 4 is coupled to the controller 2 of the display device 3 shown in FIG. 4 can include a processor or the like to input data to the controller 2 to render an image. The electronic device 5 may be a portable device such as a PDA, notebook computer, tablet computer, cellular phone, or a desktop computer.

[0056] The present invention provides a method for accurately forming LDD structure of TFT by adjusting the width and thickness of the gate insulating layer and the energy of the implantation. Additional masks to define a pattern of LDD are not required, and errors from misalignment of the mask are avoided.

[0057] While the invention has been described by way of example and in terms of the preferred embodiments, it is to be understood that the invention is not limited to the disclosed embodiments. To the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Therefore, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements. 

What is claimed is:
 1. A method of forming a semiconductor device, comprising the steps of: providing a semiconductor layer; providing a first masking layer over a first region of the semiconductor layer, said first masking layer comprising a material that provide a permeable barrier to a dopant; and exposing the semiconductor layer, including the first region covered by the first masking layer, to the dopant, wherein the first region covered by the first masking layer is lightly doped with the dopant in comparison to a second region not covered by the first masking layer.
 2. The method as in claim 1, further comprising the step of prior to exposing to the dopant, providing a second masking layer over a portion of the first masking layer corresponding to a third region of the semiconductor layer, the second masking layer is impermeable to the dopant, wherein the third region is not doped when the semiconductor layer including the second masking layer is exposed to dopant.
 3. The method as in claim 2, wherein the semiconductor device is a TFT, and wherein the first region of the semiconductor corresponds to a lightly doped drain structure of the TFT, the second region of the semiconductor corresponds to a heavily doped source/drain structure of the TFT, and the third region of the semiconductor corresponds to a channel of the TFT.
 4. The method as in claim 3, wherein the first masking layer comprises a gate insulating layer of the TFT.
 5. The method as in claim 4, wherein the second masking layer comprises a gate layer of the TFT.
 6. A method of forming a semiconductor device, comprising the steps of: forming first and second semiconductor structures, each comprising the steps of: providing a semiconductor layer; providing a first masking layer over a first region of the semiconductor layer, said first masking layer comprising a material that is provides a permeable barrier to dopant; and exposing the semiconductor layer, including the first region covered by the first masking layer, to a first dopant, wherein the first region covered by the first masking layer is lightly doped with the first dopant in comparison to a second region not covered by the first masking layer; wherein the first and second semiconductor structures are adjacent, and each second region includes first and second parts, and wherein the first part of the second region of the first semiconductor structure is connected to the first part of the second region of the second semiconductor structure, in a common structure joining the semiconductor structures.
 7. The method as in claim 6, further comprising the steps of: covering the common structure with a dopant blocking layer; exposing the semiconductor layer to a second dopant, including the first region covered by the first masking layer, the first part of the second region covered by the dopant blocking layer, and the second part of the second region not covered by the dopant blocking layer, wherein the first region covered by the first masking layer and the first part of the second region are further doped, wherein the first region covered by the first masking layer is lightly doped with the second dopant in comparison to the second part of the second region.
 8. The method as in claim 6, further comprising the step of prior to exposing to the dopant, providing a second masking layer over a portion of the first masking layer corresponding to a third region of the semiconductor layer, the second masking layer is impermeable to the dopant, wherein the third region is not doped when the semiconductor layer including the second masking layer is exposed to dopant.
 9. The method as in claim 8, wherein the semiconductor device is a TFT, and wherein the first region of the semiconductor corresponds to a lightly doped drain structure of the TFT, the second region of the semiconductor corresponds to a heavily doped source/drain structure of the TFT, and the third region of the semiconductor corresponds to a channel of the TFT.
 10. The method as in claim 9, wherein the first masking layer comprises a gate insulating layer of the TFT.
 11. The method as in claim 10, wherein the second masking layer comprises a gate layer of the TFT.
 12. A self-aligned LDD TFT, comprising: a substrate; a semiconductor layer having a channel region formed on the substrate, wherein a first doping region is formed on both sides of the channel region and a second doping region is formed on both sides of the first doping region; agate insulating layer formed on the semiconductor layer, wherein the gate insulating layer covers the channel region and the first doping region; and a gate formed on the gate insulating layer corresponding to the channel region.
 13. The self-aligned LDD TFT of claim 12, wherein the thickness of gate insulating layer is about 200 to 10000 Å.
 14. The self-aligned LDD TFT of claim 12, wherein the first doping region is an LDD area, the second doping region is a S/D area, and the concentration of the first doping region is lower than in the second doping region.
 15. A thin film transistor having a multi-gate structure, comprising: a substrate; an active layer formed on the substrate and comprising: a first lightly doped region; a second lightly doped region and a third lightly doped region formed laterally adjacent to the first lightly doped region respectively; a first channel region and a second channel region extending laterally away from the second lightly doped region and the third lightly doped region respectively; a fourth lightly doped region and a fifth lightly doped region extending laterally away from the first channel region and the second channel region respectively; and a first heavily doped region and a second heavily doped region extending laterally away from the fourth lightly doped region and the fifth lightly doped region respectively; a first gate insulating layer formed on the active layer and comprising: a central region covering the first channel region of the active layer; a first shielding region covering the fourth lightly doped region of the active layer; and a second shielding region covering the second lightly doped region of the active layer; a second gate insulating layer formed on the active layer and comprising: a central region covering the second channel region of the active layer; a first shielding region covering the third lightly doped region of the active layer; and a second shielding region covering the fifth lightly doped region of the active layer; a first gate layer covering the central region of the first gate insulating layer; and a second gate layer covering the central region of the second gate insulating layer.
 16. The thin film transistor having a multi-gate structure as claimed in claim 15, wherein, the margin of the second lightly doped region is substantially aligned to the edge of the second shielding region of the first gate insulating layer; the margin of the third lightly doped region is substantially aligned to the edge of the first shielding region of the second gate insulating layer; the margin of the fourth lightly doped region is substantially aligned to the edge of the first shielding region of the first gate insulating layer; and the margin of the fifth lightly doped region is substantially aligned to the edge of the second shielding region of the second gate insulating layer.
 17. The thin film transistor having a multi-gate structure as claimed in claim 15, wherein the second lightly doped region and the third lightly doped region have the same doping concentration and length.
 18. The thin film transistor having a multi-gate structure as claimed in claim 15, wherein the fourth lightly doped region and the fifth lightly doped region have the same doping concentration and length.
 19. The thin film transistor having a multi-gate structure as claimed in claim 15, wherein, each of the first lightly doped region, the fourth lightly doped region and the fifth lightly doped region has a doping concentration of 1×10¹²˜1×10¹⁴ atom/cm²; each of the second lightly doped region and third lightly doped region has a doping concentration less than 1×10¹³ atom/cm²; and each of the first heavily doped region and second heavily doped region has a doping concentration of 1×10¹⁴˜1×10¹⁶ atom/cm².
 20. The thin film transistor having a multi-gate structure as claimed in claim 15, wherein the first, second, third, fourth and fifth lightly doped regions and the first and second heavily doped regions are the same conductive type.
 21. A display device, comprising: a display panel comprising a self-aligned LDD TFT, comprising: a substrate; a semiconductor layer having a channel region formed on the substrate, wherein a first doping region is formed on both sides of the channel region and a second doping region is formed on both sides of the first doping region; a gate insulating layer formed on the semiconductor layer, wherein the gate insulating layer covers the channel region and the first doping region; and a gate formed on the gate insulating layer corresponding to the channel region; and a controller coupled to the display panel to control the display panel to render an image in accordance an input.
 22. An electronic device, comprising: a display panel comprising a self-aligned LDD TFT, comprising: a substrate; a semiconductor layer having a channel region formed on the substrate, wherein a first doping region is formed on both sides of the channel region and a second doping region is formed on both sides of the first doping region; a gate insulating layer formed on the semiconductor layer, wherein the gate insulating layer covers the channel region and the first doping region; and a gate formed on the gate insulating layer corresponding to the channel region; and a controller coupled to the display panel to control the display panel to render an image in accordance an input; and an input device couple to the controller of the display device to render an image. 